industrial repair agent > BD218 chemical wear resistant repair agent ceramic coating

BD218 chemical wear resistant repair agent ceramic coating

BD218 chemical abrasion wear resistant repair agent epoxy ceramic coating

product description of our BD218 wear abrasion chemical resistant ceramic epoxy coating repairing agent:
BD218 chemical wear resistant repairing agent epoxy ceramic coating is the high performance wear&corrosion resistant
polymerization ceramic material compounded by high performance wear&corrosion resistant material
(such as:ceramic,silicon carbide, silicon carbide, titanium alloy) and modified toughening heat resistant resin.
It’s widely used in repairing and pre-protecting of high duty coarse particles erosive wear of the pump body,fan shell,
pipeline screw conveyor and so on.

performance index:

product name	physical state	standard packaging	Volume (cm3)	operational time limit (25℃)	Time can be put into use (25℃)
BD218 wear chemical resistant repair agent epoxy coatings	paste	500g/set Two-components)	240	45min	24h

color	density (g/cm3)	compressive strength (Mpa) GB1041-2008	tensile strength (Mpa) GB6329-2008	shear strength (Mpa) GB7124-2008	bending strength (Mpa) GB1042-1999	working temperature （℃）
gray	2.43	115	39	23	54	-60～160

How to use:
1.Surface treatment: Do coarsening treatment on the pending-repair area, grinding with angle grinder or sand blasting and so on, the surface after coarsening treatment should be cleaned,
the surface after this treatment should be the one coarsening,dry and fresh substrates,should be no greasy dirt and dust.

2.Preparation:According to weight ratio 8:1 or volume ratio 4:1, make A and B two components mix uniformly,
and use it up within 30 min. According to the actual temperature,configuration can be appropriately a little more in winter,
proper less in summer.If the temperature is too low,you can properly heat up the A component to reduce viscosity for
easy to configure.

3.Coating: The suitable coating thickness of BD218 anti wear abrasion epoxy ceramic coating repair agent is 4-8mm.
Make mixed-up material spread coating on the pending-repair area layer by layer, the first layer should be compacted,
make it infiltrate fully with the substrates.Repair the surface to be smooth after the coating spreading in the suitable size
or use BD406 corrosion resistant repairing agent to coat on the surface of the coating, this material can’t do machining,
so you should pay attention to controlling the coating thickness to avoid appearing interference phenomenon in the assembly.

4.Curing: Cure for 24 hours at the temperature of 25 degree before using. If the temperature is low,should heat it up or prolong curing time to promote the curing.
General construction in winter,you can use iodine tungsten lamp do irradiation heating with 40cm distance from the coating.

Packaging specification:
Two-component,500g/set,packed in a common plastic drum,8 sets/carton or 16 sets/carton.

Transportation and storage:
Sealed storage in the cool and dry place.The warranty period is 24 months.Avoid placing it upside down,
knocking against and transporting it as a non-dangerous product during transportation.

Product packaging photo of BD218 anti chemical corrosion wear resistant repair compound ceramic epoxy coating: